Refractory Material--------High Alumina Cement (Alumina Cement)

High Alumina Cement CA50-G9

 

CA50-G9 is a type of high strength aluminate cement,it is production requires raw materials of high quality which must be well selected in order to reduce the impurities.After calcined in rotary kilns with perfect control of the temperature,the strength of CA50-G9 is nearly doubled of that of CA50-G5,that is,the compressive strength(3 day)of CA50-G9 reaches to 85-95 MPa or even higher.other physical characters are also improved.the quality is as good as that of overseas products or even better while the price is much lower.

we have been producing CA50-G9 aluminate cement in large scale with steady quality for both domestic and foreign markets and win praises of the buyers.

Chemical composition
Al2O3
%
~55
SiO2
¡Ü6.0
Fe2O3
¡Ü2.5
CaO
¡Ý33.0
Physical properties
fineness
0.045mm residue
%
-
Blaine
m2/kg
¡Ý400
setting time
initial
min
¡Ý90
final
h
¡Ü6
Flexural strength
1d
Mpa
¡Ý8.0
3d
¡Ý10.0
Compressive strength
1d
Mpa
>70
3d
>80

Testing method

Chemical Composition:According with GB/T205 for "High Alumina Cement".

Blaine:According with GB/T8074 for "High Alumina Cement".

Fineness:According with GB/T1345 with screen of 0.045mm for "High Alumina Cement"..

Setting time:According with the addenda A of GB/TGB201-2000 for "High Alumina Cement".

 

Packing:

Adopted specified by GB9774 cement packing sack,25kg or 50kg in PE bag with a complex bag of woven plastic and kraft paper outside.Other kind of bags can be supplied according with the agreements of the buyer and the seller.

Note

Keep in dry conditions and prevent humidity during storage and transportation.Don't mix other variety of cements.

 

 

 